취급재질 및 화학조성 - 유럽규격(DIN TABLE 11 ~ TABLE 20)

작성일 : 2020.04.09 조회수 : 2,000
　　　Table 11 ㅡCuZn25AI5Mn4Fe3-B (CB762S) and CuZn25AI5Mn4Fe3-C (CC762S)　　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　
Al
4,07,03,07,0Sand　　　　　　　　　
　Cu60,066,060,067,0ㅡ GS750 450 8 180 　
　Fe1,53,51,54,0　　　　　　
　Mn3,05,02,55,0Permanent　　　　　　　　　
　Niㅡ2,7ㅡ3,0mould　　　　　　　　　
　　　　　　ㅡ GM7504808180　
　ZnRemainderRemainderCentrifugal　　　　　　　　　
　Pㅡ0,02　0,03ㅡ GZ750 480 5 190 　
　Pb─0,20─0,2　　　　　　
　Sbㅡ0,03ㅡ0,03Continuous　　　　　　　　　
　Siㅡ0,08ㅡ0,1ㅡGC7504805190　
　Snㅡ0,20ㅡ0,2　　　　　　　　　　
　alncluding nickel　
　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 12ㅡ CuZn32AI2Mn2Fe1-B(CB763S) and CuZn32AI2Mn2Fe1-C (CC763S)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　
Al
1,02,51,02,5Sand　　　　　　　　　
　Cu59,067,059,067,0ㅡ GS430 150 10 100 　
　Fe0,52,00,52,0　　　　　　
　Mn1,03,51,03,5　　　　　　　　　　
　Niㅡ2,5ㅡ2,5　　　　　　　　　　
　Pbㅡ1,5ㅡ1,5Pressure die　　　　　
　Siㅡ1,0ㅡ1,0cast　　　　　
　Snㅡ1,0ㅡ1,0ㅡ GP(440)(330)(3)(130)　
　ZnRemainderRemainder(see note)　　　　　
　Sbㅡ0,08ㅡ0,08　　　　　　　　　　
　NOTEThe mechanical properties for pressure die castings (shown bracketed) are not mandatory requirements,　
　　but are given for information only (see note 4 of 6.2).　
　alncluding nickel　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 13ㅡ CuZn34Mn3AI2Fe1-B(CB764S) and CuZn34Mn3AI2Fe1-C (CC764S)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　
Al
1,53,01,03,0Sand　　　　　　　　　
　Cu55,065,055,066,0ㅡ GS600 250 15 140 　
　Fe
0,8
2,0
0,5
2,5　　　　　　
　Mn1,03,51,04,0　　　　　　　　　　
　Niㅡ2,7ㅡ3,0Permanent　　　　　　　　　
　ZnRemainderRemaindermould60026010140　
　Pㅡ0,02ㅡ0,03ㅡ GM　　　　　
　Pbㅡ0,2ㅡ0,3Centrifugal　　　　　
　Sbㅡ0,05ㅡ0,05ㅡ GZ620 260 14 150 　
　Siㅡ0,08ㅡ0,1　　　　　　　　　　
　Snㅡ0,3ㅡ0,3　　　　　　　　　　　
　alncluding nickel　
　bFor permanent mould casting, the minimum manganese content shall be 0,3 % foe ingots and castings.　　　　
　　　　　　　　　　　　　　　　　
　　　Table 14ㅡ CuZn35Mn2AI1Fe1-B(CB765S) and CuZn35Mn2AI1Fe1-C (CC765S)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　
Al
0,72,20,52,5Sand　　　　　　　　　
　Cu56,064,057,065,0ㅡ GS450 170 20 110 　
　Fe
0,5
1,8
0,5
2,0　　　　　　
　Mn0,52,50,53,0Permanent　　　　　　　　　
　Niㅡ6,0ㅡ6,0mould　47520018110　
　Snㅡ0,8ㅡ1,0ㅡ GM　　　　　　　　　
　ZnRemainderRemainderCentrifugal　　　　　
　Pㅡ0,02ㅡ0,03ㅡ GZ500 200 18 120 　
　Pbㅡ0,5ㅡ0,5Continuous　　　　　　　　　
　Sbㅡ0,08ㅡ0,08ㅡ GC50020018120　
　Siㅡ0,10ㅡ0,1　　　　　　　　　　　
　NOTEFor certain applications a minimum proportion of alpha-phase in the microstructure of castings is required　
　　(SEE 6.4).　
　alncluding nickel　
　bFor permanent mould castings, the minimum manganese content shall be 0,3 % for ingots and castings.　
　　　　　　　　　　　　　　　　　
　　　Table 15ㅡ CuZn37AI1-B(CB766S) and CuZn37AI1-C (CC766S)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　
Al
0,61,80,31,8Permanent　　　　　　　　　
　Cu60,063,060,064,0mould　　　　　　
　Niㅡ1,8ㅡ2,0ㅡ GM45017025105　
　ZnRemainderRemainder　　　　　　　　　　　
　Feㅡ0,4ㅡ0,5　　　　　　　
　Mnㅡ0,4ㅡ0,5　　　　　　　　　　　
　Pㅡ0,02ㅡㅡ　　　　　　　
　Pbㅡ0,4ㅡ0,50　　　　　　
　Sbㅡ0,05ㅡ0,1　　　　　　　　　　
　Siㅡ0,5ㅡ0,6　　　　　　
　Snㅡ0,4ㅡ0,50　　　　　　　　　　　
　alncluding nickel　
　　　　　　　　　　　　　　　　　
　　　Table 16ㅡ CuZn38AI-B(CB767S) and CuZn38AI-C (CC767S)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　
Al
0,10,80,10,8Permanent　　　　　　　　　
　Cu59,064,059,064,0mould　　　　　　
　Niㅡ0,8ㅡ1,0ㅡ GM3801303075　
　ZnRemainderRemainder　　　　　　　　　　　
　Feㅡ0,4ㅡ0,5　　　　　　　
　Mnㅡ0,4ㅡ0,5　　　　　　　　　　　
　Pㅡ0,05ㅡㅡ　　　　　　　
　Pbㅡ0,1ㅡ0,1　　　　　　
　Siㅡ0,05ㅡ0,2　　　　　　
　Snㅡ0,1ㅡ0,1　　　　　　　　　　　
　alncluding nickel　
　　　　　　　　　　　　　　　　　
　　　Table 17ㅡ CuSn10-B(CB480K) and CuSn10-C (CC480K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Cu88,590,588,090,0Sand　　　　　　　　　
　Niㅡ1,8ㅡ2,0ㅡ GS250 130 18 70 　
　Pㅡ0,05ㅡ0,2　　　　　　
　Pbㅡ0,8ㅡ1,0Permanent　　　　　　　　　
　Sn9,311,09,011,0mould　2701601080　
　AIㅡ0,01ㅡ0,01ㅡ GM　　　　　　　　　
　Feㅡ0,15ㅡ0,2Continuous　　　　　
　Mnㅡ0,10ㅡ0,10ㅡ GC280 170 10 80 　
　Sㅡ0,04ㅡ0,05　　　　　　　　　　　
　Sbㅡ0,15ㅡ0,2Centrifugal　　　　　
　Siㅡ0,01ㅡ0,02ㅡ GZ2801601080　
　Znㅡ0,5ㅡ0,5　　　　　　　　　　　
　alncluding nickel　
　　　　　　　　　　　　　　　　　
　　　Table 18ㅡ CuSn11P-B(CB481K) and CuSn11P-C (CC481K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　
Cu
87,089,387,089,5Sand　　　　　　　　　
　P0,61,00,51,0ㅡ GS250 130 5 60 　
　Sn10,211,510,011,5Permanent　　　　　
　Alㅡ0,01ㅡ0,01mould　　　　　　　　　　
　Feㅡ0,10ㅡ0,10ㅡ GM310170285　
　Mnㅡ0,05ㅡ0,05　　　　　　　　　　　
　Niㅡ0,10ㅡ0,10Continuous　　　　　
　Pbㅡ0,25ㅡ0,25ㅡ GC350 170 5 85 　
　Sㅡ0,05ㅡ0,05　　　　　　　　　　　
　Sbㅡ0,05ㅡ0,05Centrifugal　　　　　
　Siㅡ0,01ㅡ0,01ㅡ GZ330170485　
　Znㅡ0,05ㅡ0,05　　　　　　　　　　　
　aFor sand castings for non-bearing applications the phosphorus may be restricted to 0,15 max. [see 5 h)].　
　　　　　　　　　　　　　　　　　
　　　Table 19ㅡ CuSn11Pb2-B(CB482K) and CuSn11Pb2-C (CC482K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　Cu83,586,583,587,0Sand　　　　　　　　　
　Niㅡ2,0ㅡ2,0ㅡ GS240 130 5 80 　
　Pㅡ0,05ㅡ0,40　　　　　　　
　Pb0,72,50,72,5　　　　　　　　　　　
　Sn10,712,510,512,5Centrifugal　　　　　
　Znㅡ2,0ㅡ2,0ㅡ GZ280150590　
　Alㅡ0,01ㅡ0,01　　　　　　　
　Feㅡ0,15ㅡ0,20　　　　　　　
　Mnㅡ0,2ㅡ0,2Continuous　　　　　　　　　
　Sㅡ0,08ㅡ0,08ㅡ GC280150590　
　Sbㅡ0,20ㅡ0,2　　　　　　　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 20ㅡ CuSn12-B(CB483K) and CuSn12-C (CC483K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.
max.
min.
max.
　min.min.min.min.　
　Cu85,588,585,088,5Sand　　　　　　　　　
　Niㅡ2,0ㅡ2,0ㅡ GS260 140 7 80 　
　Pㅡ0,20ㅡ0,60　　　　　　　
　Pb
ㅡ
0,6
ㅡ
0,7Permanent　　　　　　　　　
　Sn11,213,011,013,0mould　270150580　
　Alㅡ0,01ㅡ0,01ㅡ GM　　　　　　　　　　
　Feㅡ0,15ㅡ0,2Continuous　　　　　
　Mnㅡ0,2ㅡ0,2ㅡ GC300 150 6 90 　
　Sㅡ0,05ㅡ0,05　　　　　　　　　　　
　Sbㅡ0,15ㅡ0,15Centrifugal　　　　　
　Siㅡ0,01ㅡ0,01ㅡ GZ280150590　
　Znㅡ0,4ㅡ0,5　　　　　　　　　　　
　aFor continuous castings and centrifugal castings, the minimum tin content content for ingots shall be 10,7% and for 　
　　castings 10,5% and the maximum copper content content for ingots and castings shall be 89,0%