취급재질 및 화학조성 - 유럽규격(DIN TABLE 21 ~ TABLE 28)

작성일 : 2020.04.09 조회수 : 2,133
　　　　　　　　　　　　　　　　　
　　　Table 21ㅡ CuSn12Ni2-B(CB484K) and CuSn12Ni2-C (CC484K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　Cu84,087,084,587,5Sand　　　　　　　　　
　Ni1,52,41,52,5ㅡ GS280 160 12 85 　
　Pㅡ0,050,050,40　　　　　　　
　Sn11,313,011,013,0Centrifugal　　　　　　　　　
　Alㅡ0,0,1ㅡ0,01ㅡ GZ300180895　
　Feㅡ0,15ㅡ0,20　　　　　　　　　　　
　Mnㅡ0,10ㅡ0,2　　　　　　
　Pbㅡ0,2ㅡ0,3　　　　　　
　Sㅡ0,04ㅡ0,05Continuous　　　　　　　　　
　Sbㅡ0,05ㅡ0,1ㅡ GC3001801095　
　Siㅡ0,01ㅡ0,01　　　　　　　
　Znㅡ0,3ㅡ0,4　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 22ㅡ CuSn3Zn8Pb5-B(CB490K) and CuSn3Zn8Pb5-C (CC490K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Cu81,085,581,086,0Sand　　　　　　　　　
　Niㅡ2,0ㅡ2,0ㅡ GS180 85 15 60 　
　Pㅡ0,03ㅡ0,05　　　　　　　
　Pb3,55,83,06,0　　　　　　　　　　　
　Sn2,23,52,03,5Centrifugal　　　　　　　　　
　Zn7,510,07,09,5ㅡ GZ　2201001270　
　Alㅡ0,01ㅡ0,01　　　　　　
　Feㅡ0,50ㅡ0,5Continuous　　　　　
　Sㅡ0,08ㅡ0,10ㅡ GC　2201001270　
　Sbㅡ0,25ㅡ0,30　　　　　　　　　　　
　Siㅡ0,01ㅡ0,01　　　　　　　
　alncluding nickel　　　
　　　　　　　　　　　　　　　　　
　　　Table 23aㅡ CuSn5Zn5Pb2-B(CB499K) and CuSn5Zn5Pb2-C (CC499K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　Cu84,087,584,088,0Sand　　　　　　　　　
　Niㅡ0,60ㅡ0,60ㅡ GS200 90 13 60 　
　Pㅡ0,03ㅡ0,04　　　　　　　
　Pbㅡ3,0ㅡ3,0Permanent　　　　　　　　　
　Sn4,26,04,06,0mould　220110665　
　　　　　　ㅡ GM　　　　　　　　　
　Zn4,56,54,06,0Centrifugal　　　　　　　　　
　Alㅡ0,01ㅡ0,01ㅡ GZ　2501101365　
　Asㅡ0,03ㅡ0,03　　　　　　　
　Biㅡ0,02ㅡ0,02　　　　　　　　　　　
　Cdㅡ0,02ㅡ0,02　　　　　　　　　　　
　Crㅡ0,02ㅡ0,02　　　　　　　
　Feㅡ0,30ㅡ0,30　　　　　　　　　　　
　Sㅡ0,04ㅡ0,04Continuous　　　　　　　　　
　Sbㅡ0,10ㅡ0,10ㅡ GC　2501101365　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　NOTEFor drinking water applications no other single element should be more than 0,02%. The sum of these single　　　　
　　elements should not exceed 0,25%.　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 23bㅡ CuSn5Zn5Pb5-B(CB491K) and CuSn5Zn5Pb5-C (CC491K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Cu83,086,583,087,0Sand　　　　　　　　　
　Niㅡ2,0ㅡ2,0ㅡ GS200 90 13 60 　
　Pㅡ0,03ㅡ0,10　　　　　　　
　Pb4,25,84,06,0Permanent　　　　　　　　　
　Sn4,26,04,06,0mould　220110665　
　　　　　　ㅡ GM　　　　　　　　　
　Zn4,56,54,06,0Centrifugal　　　　　　　　　
　Alㅡ0,01ㅡ0,01ㅡ GZ　2501101365　
　Feㅡ0,25ㅡ0,3　　　　　　　　　　　
　Sㅡ0,08ㅡ0,10Continuous　　　　　　　　　
　Sbㅡ0,25ㅡ0,25ㅡ GC　2501101365　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　alncluding nickel　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 24ㅡ CuSn7Zn2Pb3-B(CB492K) and CuSn7Zn2Pb3-C (CC492K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Cu85,088,585,089,0Sand　　　　　　　　　
　Niㅡ2,0ㅡ2,0ㅡ GS230 130 14 65 　
　Pㅡ0,03ㅡ0,10　　　　　　　
　
Pb
2,73,52,53,5Permanent　　　　　　　　　
　Sn6,28,06,08,0mould　2301301270　
　　　　　　ㅡ GM　　　　　　　　　
　Zn1,73,21,53,0Centrifugal　　　　　　　　　
　Alㅡ0,01ㅡ0,01ㅡ GZ　2601301270　
　Feㅡ0,25ㅡ0,2　　　　　　　　　　　
　Sㅡ0,08ㅡ0,10Continuous　　　　　　　　　
　Sbㅡ0,25ㅡ0,25ㅡ GC　2701301270　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　alncluding nickel　
　b(Tin+½ nickel) content shall be in the range 7,0 % to 8,0 %　　　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 25ㅡ CuSn7Zn4Pb7-B(CB493K) and CuSn7Zn4Pb7-C (CC493K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.
max.
min.
max.
　min.min.min.min.　
　Cu81,084,581,085,0Sand　　　　　　　　　
　Niㅡ2,0ㅡ2,0ㅡ GS230 120 15 60 　
　Pㅡ0,03ㅡ0,10　　　　　　　
　Pb
5,2
8,0
5,0
8,0Permanent　　　　　　　　　
　Sn6,28,06,08,0mould　2301201260　
　　　　　　ㅡ GM　　　　　　　　　
　Zn2,35,02,05,0Continuous　　　　　　　　　
　Alㅡ0,01ㅡ0,01ㅡ GC　2601201270　
　Feㅡ0,20ㅡ0,2　　　　　　　　　　　
　Sㅡ0,08ㅡ0,10Centrifugal　　　　　　　　　
　Sbㅡ0,30ㅡ0,3ㅡ GZ　2601201270　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　alncluding nickel　
　bFor continuous castings and centrifugal castings, the minimum tin content for ingots shall be 5,4 % and for castings　　　
　　5,2 % and the maximum copper content for ingots shall be 85,0 % and for castings 86, 0 %.　　　　　　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 26ㅡ CuSn6Zn4Pb2-B(CB498K) and CuSn6Zn4Pb2-C (CC498K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Cu86,089,586,090,0Sand　　　　　　　　　
　Niㅡ1,0ㅡ1,0ㅡ GS220 110 15 65 　
　Pㅡ0,03ㅡ0,05　　　　　　　
　Pb1,22,01,02,0Permanent　　　　　　　　　
　Sn5,76,55,56,5mould　2201101270　
　　　　　　ㅡ GM　　　　　　　　　
　Zn3,25,03,05,0Centrifugal　　　　　　　　　
　Alㅡ0,01ㅡ0,01ㅡ GZ　2401101270　
　Feㅡ0,25ㅡ0,25　　　　　　　　　　　
　Sㅡ0,08ㅡ0,10Continuous　　　　　　　　　
　Sbㅡ0,25ㅡ0,25ㅡ GC　2401101270　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　alncluding nickel　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 27ㅡ CuSn5Pb9-B(CB494K) and CuSn5Pb9-C (CC494K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Cu80,086,580,087,0Sand　　　　　　　　　
　Niㅡ2,0ㅡ2,0ㅡ GS160 60 7 55 　
　Pㅡ0,10ㅡ0,10　　　　　　　
　Pb8,210,08,010,0Permanent　　　　　　　　　
　Sn4,26,04,06,0mould　20080560　
　　　　　　ㅡ GM　　　　　　　　　
　Znㅡ2,0ㅡ2,0Centrifugal　　　　　　　　　
　Alㅡ0,01ㅡ0,01ㅡ GZ　20090660　
　Feㅡ0,20ㅡ0,25　　　　　　　　　　　
　Mn　0,2　0,2　　　　　　　　　　　
　Sㅡ0,08ㅡ0,10Continuous　　　　　　　　　
　Sbㅡ0,5ㅡ0,5ㅡ GC　200100960　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　alncluding nickel　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 28ㅡ CuSn10Pb10-B(CB495K) and CuSn10Pb10-C (CC495K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Cu78,081,578,082,0Sand　　　　　　　　　
　Niㅡ2,0ㅡ2,0ㅡ GS180 80 8 60 　
　Pㅡ0,10ㅡ0,10　　　　　　　
　Pb8,210,58,011,0Permanent　　　　　　　　　
　Sn9,211,09,011,0mould　220110365　
　　　　　　ㅡ GM　　　　　　　　　
　Znㅡ2,0ㅡ2,0Centrifugal　　　　　　　　　
　Alㅡ0,01ㅡ0,01ㅡ GZ　220110670　
　Feㅡ0,20ㅡ0,25　　　　　　　　　　　
　Mn　0,2　0,2　　　　　　　　　　　
　Sㅡ0,08ㅡ0,10Continuous　　　　　　　　　
　Sbㅡ0,5ㅡ0,5ㅡ GC　220110870　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　alncluding nickel