취급재질 및 화학조성 - 유럽규격 EN1982 (DIN TABLE 29 ~ TABLE 35)

작성일 : 2020.04.13 조회수 : 2,494
　　　　　　　　　　　　　　　　　
　　　Table 29ㅡ CuSn7Pb15-B(CB496K) and CuSn7Pb15-C (CC496K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Cu74,079,574,080,0Sand　　　　　　　　　
　Niㅡ2,00,52,0ㅡ GS170 80 8 60 　
　Pㅡ0,10ㅡ0,10　　　　　　　
　Pb13,217,013,017,0　　　　　　　　　　　
　Sn6,28,06,08,0Continuous　　　　　
　Znㅡ2,0ㅡ2,0ㅡ GC　20090865　
　Alㅡ0,01ㅡ0,01　　　　　　　
　Feㅡ0,20ㅡ0,25　　　　　　　　　　　
　Mn　0,20　0,20Centrifugal　　　　　　　　　
　Sㅡ0,08ㅡ0,10ㅡ GZ　20090765　
　Sbㅡ0,5ㅡ0,5　　　　　　　　　　　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　alncluding nickel　
　　　　　　　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 30ㅡ CuSn5Pb20-B(CB497K) and CuSn5Pb20-C (CC497K)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Cu70,077,570,078,0Sand　　　　　　　　　
　Ni0,52,50,52,5ㅡ GS150 70 5 45 　
　Pㅡ0,10ㅡ0,10　　　　　　　
　Pb19,023,018,023,0　　　　　　　　　　　
　Sn4,26,04,06,0Continuous　　　　　
　Znㅡ2,0ㅡ2,0ㅡ GC　18090750　
　Alㅡ0,01ㅡ0,01　　　　　　　
　Feㅡ0,20ㅡ0,25　　　　　　　　　　　
　Mnㅡ0,20ㅡ0,20Centrifugal　　　　　　　　　
　Sㅡ0,08ㅡ0,10ㅡ GZ　17080650　
　Sbㅡ0,75ㅡ0,75　　　　　　　　　　　
　Siㅡ0,01ㅡ0,01　　　　　　　　　　　
　alncluding nickel　
　　　　　　　　　　　　　　　　　
　　　Table 31ㅡ CuAl9-B(CB330G) and CuAl9-C (CC330G)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　
Al
8,210,58,010,5Permanent　　　　　　　　　
　Cu88,091,588,092,0mould　500 180 20 100 　
　Feㅡ1,0ㅡ1,2ㅡ GM　　　　　
　Mnㅡ0,50ㅡ0,50　　　　　　　　　　　
　Niㅡ1,0ㅡ1,0Centrifugal　　　　　
　Pbㅡ0,25ㅡ0,30ㅡ GZ　45016015100　
　Siㅡ0,15ㅡ0,20　　　　　　　
　Snㅡ0,25ㅡ0,30　　　　　　　　　　　
　Znㅡ0,40ㅡ0,50　　　　　　　　　　　
　alncluding nickel　
　　　　　　　　　　　　　　　　　
　　　Table 32ㅡ CuAl10Fe2-B(CB331G) and CuAl10Fe2-C (CC331G)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　Al8,710,58,510,5Sand　　　　　　　　　　
　Cu83,089,083,089,5ㅡ GS　500 180 18 100 　
　Fe1,53,31,53,5Permanent　　　　　
　Mnㅡ1,0ㅡ1,0mould　60025020130　
　　　　　　ㅡ GM　　　　　　　　　
　Niㅡ1,5ㅡ1,5Centrifugal　　　　　
　Mgㅡ0,05ㅡ
0,05
ㅡ GZ　55020018130　
　Pbㅡ0,03ㅡ0,10　　　　　　　
　Siㅡ0,15ㅡ0,2Continuous　　　　　
　Snㅡ0,20ㅡ0,20ㅡ GC55020015130　
　Znㅡ0,50ㅡ0,50　　　　　　　　　　　
　aFor castings intended to be welded, the maximum lead content shall be 0,03%.　
　　　　　　　　　　　　　　　　　
　　　Table 33ㅡ CuAl10Ni3Fe2-B(CB332G) and CuAl10Ni3Fe2-C (CC332G)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Al8,7
10,5
8,5
10,5
Sand　　　　　　　　　　
　Cu80,085,580,086,0ㅡ GS　500 180 18 100 　
　Fe1,02,81,03,0Permanent　　　　　
　Mnㅡ2,0ㅡ2,0mould　60025020130　
　
　
　　　　ㅡ GM　　　　　　　　　
　Ni1,54,01,54,0Centrifugal　　　　　
　Mgㅡ0,05ㅡ
0,05
ㅡ GZ　55022020120　
　Pbㅡ0,03ㅡ0,10　　　　　　　
　Siㅡ0,15ㅡ0,2Continuous　　　　　
　Snㅡ0,20ㅡ0,20ㅡ GC55022020120　
　Znㅡ0,50ㅡ0,50　　　　　　　　　　　
　aFor castings for sea-water applications, the aluminium content shall be such that A1 % <(8,2+0,5 Ni % ).　
　bFor permanent mould castings, the maximum copper content for ingots and castings shall be 88,5 %.　
　cFor castings intende to be welded, the maximum lead content shall be 0,03 %.　
　　　　　　　　　　　　　　　　　
　　　Table 34ㅡ CuAl10Fe5Ni5-B(CB333G) and CuAl10Fe5Ni5-C (CC333G)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　Al8,810,08,510,5Sand　　　　　　　　　　
　
Cu
76,082,576,083,0ㅡ GS　600 250 13 140 　
　Fe4,05,34,05,5　　　　　　　
　
Mn
ㅡ2,5ㅡ3,0Permanent　　　　　　　　　
　Ni4,05,54,06,0mould　　　7　　
　Biㅡ0,01ㅡ0,01ㅡ GM　650280　150　
　Crㅡ0,05ㅡ0,05Centrifugal　　　　　　　　　
　Mgㅡ0,05ㅡ0,05ㅡ GZ　65028013150　
　Pbㅡ0,03ㅡ0,03　　　　　　　
　Siㅡ0,10ㅡ0,1Continuous　　　　　
　Snㅡ0,1ㅡ0,1ㅡ GC65028013150　
　Znㅡ0,40ㅡ0,50　　　　　　　　　　　
　aFor permanent mould castings, the minimum iron content of ingots and castings shall be 3,0 % and the minimum　
　nickel content shall be 3,7 %.　　　　
　　　　　　　　　　　　　　　　　
　　　Table 35ㅡ CuAl11Fe6Ni6-B(CB334G) and CuAl11Fe6Ni6-C (CC334G)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　
　
min.max.min.max.　min.min.min.min.　
　Al10,312,010,012,0Sand　　　　　　　　　　
　Cu72,081,572,082,5ㅡ GS　680 320 5 170 　
　Fe4,27,04,07,0　　　　　　　
　Mnㅡ2,5ㅡ2,5Permanent　　　　　　　　　
　Ni4,37,54,07,5mould　　　　　　
　Mgㅡ0,05ㅡ0,05ㅡ GM　7503805185　
　Pbㅡ0,04ㅡ0,05Continuous　　　　　
　Siㅡ0,10ㅡ0,1ㅡ GC7503805185　
　Snㅡ0,20ㅡ0,2　　　　　　　　　　　
　Znㅡ0,40ㅡ0,50　　　　　　　　　　　
　aFor permanent mould castings, the minimum iron content of ingots and castings shall be 3,0 % and the minimum　
　aluminium content shall be 9,0 %. ln this case, the maximum copper content shall be 84,5 %.