취급재질 및 화학조성 - 유럽규격 EN1982 (DIN TABLE 36 ~ TABLE 40)

작성일 : 2020.04.13 조회수 : 2,537
　　　　　　　　　　　　　　　　　
　　　Table 36ㅡ CuMn11Al8Fe3Ni3-C (CC212E)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　Ala7,09,0Sand　　　　　　　　　　
　Cu68,077,0ㅡ GS　630 275 18 150 　
　Fe2,04,0　　　　　　　
　Mn8,015,0　　　　　　　　　　　
　Ni1,54,5　　　　　　　
　Mgaㅡ0,05　　　　　　　
　Pbㅡ0,05　　　　　　　
　Siㅡ0,1　　　　　　
　Snㅡ0,5　　　　　　　　　　　
　Znㅡ1,0　　　　　　　　　　　
　alngot properties for producing castings conforming to CuMn11A¹ 8Fe3Ni3-C (CC212E) are not specified in this　
　standard. The composition limits for ingots are at the discretion of the purchaser and shall be stated on the enquiry　　　
　　and order [see 5 l)].　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 37ㅡ CuNi10Fe1Mn1-B (CB380H) and CuNi10Fe1Mn1-C (CC380H)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　Cu84,5ㅡ84,5ㅡSand　　　　　　　　　　
　Fe1,21,81,01,8ㅡ GS　280 120 20 70 　
　Mn1,21,51,01,5　　　　　　　
　Ni9,211,09,011,0Centrifugal　　　　　　　　　
　Siㅡ0,10ㅡ0,10ㅡ GZ　2801002570　
　Alㅡ0,01ㅡ0,01　　　　　　　
　Cㅡ0,10ㅡ0,10Continuous　　　　　
　Nbㅡ1,0ㅡ1,0ㅡ GC2801002570　
　Pbㅡ0,03ㅡ0,03　　　　　　　　　　　
　Znㅡ0,50ㅡ0,5　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 38ㅡ CuNi30Fe1Mn1-B (CB381H) and CuNi30Fe1Mn1-C (CC381H)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　Cu64,5ㅡ64,5ㅡSand　　　　　　　　　　
　Fe0,51,50,51,5ㅡ GS　340 120 18 80 　
　Mn0,71,20,61,2　　　　　　　
　Ni29,231,029,031,0　　　　　　　　　　　
　Siㅡ0,10ㅡ0,1　　　　　　　
　Alㅡ0,01ㅡ0,01　　　　　　　
　Cㅡ0,02ㅡ0,03Centrifugal　　　　　
　Pㅡ0,01ㅡ0,01ㅡ GZ　3401201880　
　Pbㅡ0,03ㅡ0,03　　　　　　　　　　　
　Sㅡ0,01ㅡ0,01　　　　　　　　　　　
　Znㅡ0,50ㅡ0,5　　　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 39ㅡ CuNi30Cr2FeMnSi-C (CC382H)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　Cra1,52,0Sand　　　　　　　　　　
　CuRemainderㅡ GS　440 250 18 115 　
　Fe0,51,0　　　　　　　
　Mn0,51,0　　　　　　　　　　　
　Ni29,032,0　　　　　　　　　　　
　Si0,150,50　　　　　　　
　Tiㅡ0,25　　　　　　　　　　　
　Zrㅡ0,15　　　　　　　　　　　
　Alaㅡ0,01　　　　　　　
　Bㅡ0,01　　　　　　
　Biㅡ0,002　　　　　　　　　　　
　Cㅡ0,03　　　　　　　　　　　
　Mgㅡ0,01　　　　　　　　　　　
　Pㅡ0,01　　　　　　　
　Pbㅡ0,005　　　　　　　　　　　
　Sㅡ0,01　　　　　　　　　　　
　Seㅡ0,005　　　　　　　　　　　
　Teㅡ0,005　　　　　　　　　　　
　Znㅡ0,2　　　　　　　　　　　
　alngot properties for producing to CuNi30Cr2FeMnSi-C (CC382H) are not specified in this　
　standard. The composition limits for ingots are at the discretion of the purchaser and shall be stated on the enquiry 　
　and order [see 5 l)].　　　　　　　　　
　　　　　　　　　　　　　　　　　
　　　Table 40ㅡ CuNi30Fe1Mn1NbSi-C (CC383H)　　　
　Composition in %
(mass fraction)		CastingTensile0,2 %　Brinell　
　processstrengthproof strengthElongationhardness　
　and
　
0.2
A　　
　elementingotscastingsdesignationN/㎟N/㎟%HBW　
　　min.max.min.max.　min.min.min.min.　
　CuaRemainderSand　　　　　　　　　　
　Fe0,51,5ㅡ GS　440 230 18 115 　
　Mn0,61,2　　　　　　　　　　　
　Nb0,51,0　　　　　　　　　　　
　Ni29,031,0　　　　　　　
　Si0,30,7　　　　　　　　　　　
　Alaㅡ0,01　　　　　　　
　Bㅡ0,01　　　　　　
　Biㅡ0,01　　　　　　　　　　　
　Cㅡ0,03　　　　　　　　　　　
　Cdㅡ0,02　　　　　　　　　　　
　Mgㅡ0,01　　　　　　　　　　　
　Pㅡ0,01　　　　　　　
　Pbㅡ0,01　　　　　　　　　　　
　Sㅡ0,01　　　　　　　　　　　
　Seㅡ0,01　　　　　　　　　　　
　Teㅡ0,01　　　　　　　　　　　
　Znㅡ0,50　　　　　　　　　　　
　alngot properties for producing castings conforming to CuNi30Fe1NbSi-C (CC383H) are not specified in this　
　standard. The composition limits for ingots are at the discretion of the purchaser and shall be stated on the enquiry 　
　and order [see 5 l)].